鋁合金重力鑄造(zao)的缺陷(xian)分析：
鋁合金重力鑄造就是用金屬鑄造而成的工藝，從而獲得零件的鋁合金和鋁合金重力鑄造件。鋁合金重力鑄造具有流動性，收縮性，熱烈性，氣密性，鑄造應力，吸氣性。
渣是氧化夾渣多分布在鑄件的上表面，鑄型不通氣的轉角部位。斷口多呈灰白色或黃色，經x光透視或在機械加工時發現，也可在堿洗、酸洗或陽極化時發現氣(qi)(qi)(qi)(qi)孔(kong)(kong)(kong) 氣(qi)(qi)(qi)(qi)泡(pao)就(jiu)是三(san)鑄件壁內氣(qi)(qi)(qi)(qi)孔(kong)(kong)(kong)一(yi)般呈(cheng)(cheng)圓形或橢(tuo)圓形，具(ju)有(you)(you)光(guang)滑的表(biao)面，一(yi)般是發亮的氧(yang)化皮，有(you)(you)時呈(cheng)(cheng)油黃色(se)。表(biao)面氣(qi)(qi)(qi)(qi)孔(kong)(kong)(kong)、氣(qi)(qi)(qi)(qi)泡(pao)可通(tong)過噴砂(sha)發現(xian)，內部氣(qi)(qi)(qi)(qi)孔(kong)(kong)(kong) 氣(qi)(qi)(qi)(qi)泡(pao)可通(tong)過X光(guang)透視或機(ji)械加工發現(xian)氣(qi)(qi)(qi)(qi)孔(kong)(kong)(kong) 氣(qi)(qi)(qi)(qi)泡(pao)在X光(guang)底片上呈(cheng)(cheng)黑色(se)。就是鋁鑄(zhu)件縮松(song)一般產生在(zai)內澆道附近(jin)飛(fei)冒口根部厚(hou)大(da)部位、壁(bi)的(de)厚(hou)薄(bo)轉接處(chu)和具有大(da)平(ping)面(mian)的(de)薄(bo)壁(bi)處(chu)。在(zai)鑄(zhu)態時斷口為灰(hui)色，淺黃色經熱(re)處(chu)理(li)后為灰(hui)白淺黃或(huo)灰(hui)黑色在(zai)x光(guang)(guang)底片上呈云霧狀嚴重的(de)呈絲(si)狀縮松(song)可通過X光(guang)(guang)、熒光(guang)(guang)低倍 斷口等檢查方法發(fa)現。
通常分為兩種情況
1．鑄造裂紋。沿晶界發展，常伴有偏析，是一種在較高溫度下形成的裂紋在體積收縮較大的合金和形狀較復雜的鑄件容易出現
2．熱處理裂紋：由于熱處理過燒或過熱引起，常呈穿晶裂紋。常在產生應力和熱膨張系數較大的合金冷卻過劇。或存在其他冶金缺陷時產生
分析是在壓鑄件缺陷中，出現最多的是氣孔。氣孔特征。有光滑的表面，形狀是圓形或橢圓形。表現形式可以在鑄件表面、或皮下針孔、也可能在鑄件內部。
掃一掃查看手機站